| Megalon® PA66 GF30 is a 30-33% glass fiber reinforced nylon 66 offering an excellent balance of high temperature performance, dimensional stability, tensile strength, and impact resistance. This grade of Megalon is pre-colored white |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 172 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 9380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 252 | °C | ASTM D648 |
| Peak Melting Temperature | 261 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA250G15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| APEX® 90-A471R-90-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Hanwha Total PE B220A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Latigloss 66 H2 G/50 | LATI S.p.A. | Nylon 66 | Latigloss |
| OnFlex™ AF 7210-80 | PolyOne Corporation | TPE | OnFlex™ |