| EPO-TEK ® 320 is a two component, black-colored and optically opaque epoxy designed for optical, medical, and opto-electronic packaging of semiconductor devices and components. It is a widely used fiber-optic grade epoxy. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 384 | °C | TGA |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 1.80 | GPa | |
| Thixotropic Index | 5.70 | ||
| Weight Loss on Heating | |||
| 200°C | 0.27 | % | |
| 250°C | 0.45 | % | |
| 300°C | 0.80 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 55.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.9E-5 | cm/cm/°C | |
| -- 3 | 1.0E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance (300 to 2500 nm) | < 1.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 2.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 4 | Black | ||
| -- 5 | Clear/Transparent | ||
| Density | |||
| Part B | 0.868 | g/cm³ | |
| Part A | 1.10 | g/cm³ | |
| Viscosity 6(23°C) | 0.70 to 1.2 | Pa·s | |
| Curing Time (65°C) | 2.0 | hr | |
| Pot Life | 60 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Volume Resistivity (23°C) | > 1.0E+6 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® 125-15 MG | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hiprolon® 70 NN LM | Arkema | Nylon 610 | Hiprolon® |
| Huafon JF-W-3030 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| POLYfill PPH BK901010 VT2 | Polykemi AB | PP Homopolymer | POLYfill |
| Hostacom M4 N01 LG82767 | LyondellBasell Industries | PP Homopolymer | Hostacom |