Ultramid® 8253 HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lea4XC_Ultramid-8253-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8253 HS BK-102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for both injection molding and extrusion applications. It exhibits varying levels of toughness and flexibility combined with excellent thermal and chemical properties. Applications Ultramid 8253 HS BK-102 is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips fasteners, flanges, key housings as well as many flexible tubing applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | % | |
| Water Absorption | |||
| 24 hr | 1.5 | % | ASTM D570 |
| 23°C, 24 hr | 1.5 | % | ISO 62 |
| Saturation | 8.1 | % | ASTM D570 |
| Saturation, 23°C | 8.1 | % | ISO 62 |
| Equilibrium, 50% RH | 2.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 65.0 | MPa | ASTM D638 |
| Yield, 23°C | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 4.0 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2270 | MPa | ASTM D790 |
| 23°C | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 85.0 | MPa | ASTM D790 |
| 23°C | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C | 14 | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 271 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 9.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 0.710 mm | 105 | °C | |
| 0.750 mm | 105 | °C | |
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| 6.00 mm | 105 | °C | |
| RTI Imp | UL 746 | ||
| 0.710 mm | 95.0 | °C | |
| 0.750 mm | 95.0 | °C | |
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| 6.00 mm | 105 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 95.0 | °C | |
| 0.750 mm | 95.0 | °C | |
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| 6.00 mm | 105 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyopt® LM11 | Suzhou OMAY Optical Materials Co., Ltd | Film, PMMA | Polyopt® |
| UmaPET AOCMH | Ester Industries Ltd. | PET | UmaPET |
| Kumho KNB 1845 | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| Lion Idemitsu Composites PPS G561F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| LUVOCOM® 1105-8234 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |