4PROP® 9C11270
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | leLH01_4PROP-9C11270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 9C11270 is a MFI 5 70% Barium Sulphate Filled Copolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Moisture Content | < 1000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 18.0 | MPa | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® M 68 FW | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| TRANSMARE® 10HGB30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| TOTAL Polypropylene PPH 3571 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| AKROMID® A3 GF 60 1 black (2395) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| SIBUR Synthetic Rubber SBR-1706 Grade C | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |