LNP™ LUBRICOMP™ WBL36L compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ldRzcV_LNP-LUBRICOMP-WBL36L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. Also known as: LNP* LUBRICOMP* Compound WBL-4036 LE Product reorder name: WBL36L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.0 to 3.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.7 to 2.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.9 | % | ISO 294-4 |
| Flow : 24 hr | 2.4 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 4020 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 37.2 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2 |
| Break | 36.5 | MPa | ASTM D638 |
| Break | 36.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.2 | % | ASTM D638 |
| Yield | 2.4 | % | ISO 527-2 |
| Break | 3.0 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4140 | MPa | ASTM D790 |
| -- | 3900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 68.9 | MPa | ASTM D790 |
| -- | 75.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.66 | ||
| vs. Itself - Static | 0.63 | ||
| Wear Factor - Washer | 25.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 3.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D4812 |
| 23°C 3 | 19 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.50 | J | ASTM D3763 |
| -- | 1.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 189 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 184 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 94.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAGLIDE HI | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAGLIDE |
| Moplen HP456H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Xuchuan 2000/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| HiFill® PA6/6 CM25 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Karina IVORY PVC COMPOUND -E 60880-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |