Trademark PS PS820
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Trademark Plastics Corporation |
| Trademark: | Trademark PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ldCiap_Trademark-PS-PS820.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Properties:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(3.18 mm) | 2000 | MPa | ASTM D638 |
| Tensile Strength 3(3.18 mm) | 22.4 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.18 mm) | 44 | % | ASTM D638 |
| Flexural Modulus 5(6.35 mm) | 1950 | MPa | ASTM D790 |
| Flexural Strength 6(6.35 mm) | 40.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 7(1.8 MPa, Unannealed, 6.35 mm) | 77.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 15.6 to 65.6 | °C |
| Note Message | |
|---|---|
| 1 . | 24 hours |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | 2.5 mm/min |
| 6 . | 2.5 mm/min |
| 7 . | (F0) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITIKA Nylon 6 RUN35-C25 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| COPYLENE® CH085S | Phillips 66 | PP Homopolymer | COPYLENE® |
| Daicel PP PG8N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Formolene® E900 | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| LEXAN™ LUX2910T resin | SABIC Innovative Plastics | PC | LEXAN™ |