LNP™ THERMOCOMP™ DF004ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lYx3ri_LNPTHERMOCOMPDF004ERcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF004ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release. Also known as: LNP* THERMOCOMP* Compound DF-1004 EM MR Product reorder name: DF004ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.25 - 0.45 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 97.0 | MPa | ISO 527-2/5 |
| Fracture | 120 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.6 | % | ISO 527-2/5 |
| Fracture | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 5500 | MPa | ISO 178 |
| Flexural Stress | 178 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 144 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 140 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® S4740 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Prime ABS Weather-X 200 | Primex Plastics Corporation | ABS+Acrylic | Prime ABS Weather-X |
| HAIPLEN H10 T4 HT | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Grilon® TSC-10/4 EC black 9832 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Lucene™ LC565 | LG Chem Ltd. | TPO (POE) | Lucene™ |