Plexar® PX5125
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lYrvYr_Plexar-PX5125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 51 µm, blown film | 10.7 | MPa | ASTM D882 |
| MD : Broken, 51 µm, blown film | 25.1 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 23.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : yield, 51 µm, blow film | 20 | % | ASTM D882 |
| TD : yield, 51 µm, blow film | 9.0 | % | ASTM D882 |
| MD : Broken, 51 µm, blown film | 640 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 730 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, blown film | 320 | g | ASTM D1922 |
| TD : 51 µm, blown film | 690 | g | ASTM D1922 |
| Water Vapor Transmission Rate (100% RH, 51 µm, Blown Film) | 7.5 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Additional Information |
|---|
| A process melt temperature above 410°F (210°C) is recommended to ensure adhesion between adherents. More specific suggestions can be made only when equipment, process parameters and conditions of use are known. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | > 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4088 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| LubriOne™ SF-30CF/15T BLACK | PolyOne Corporation | PPS | LubriOne™ |
| LUVOCOM® 19-7748 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| Therma-Tech™ TT9200-5010 EC Anthracite | PolyOne Corporation | PPS | Therma-Tech™ |
| LNP™ STAT-KON™ DEL22P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |