Lumid® GP2330B(W)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lY9Ym6_Lumid-GP2330B-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Applications Automotive(Air Intake Manifold, Cylinder Head Cover) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 191 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 9320 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 279 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 260 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 250 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 120 | °C | |
| 1.50 mm | 110 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 120 | °C | |
| 1.50 mm | 110 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 120 | °C | |
| 1.50 mm | 110 | °C | |
| 3.00 mm | 120 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure 5 | 0.981 to 2.94 | MPa | |
| Screw Speed | 60 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4F 809-SB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Starflam AFR470X2 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Baoding 76T90 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Formolene FORMAX® L91507E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| LNP™ THERMOCOMP™ KF006 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |