VAMPEEK A 5010
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lWFNbO_VAMPEEK-A-5010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PEEK 50% glass fiber reinforced, low viscosity, UL 94 V0, halogen and red phosphorus free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 | % | |
| Across Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 175 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 330 | °C | ASTM D648A |
| Vicat Softening Temperature | 335 | °C | ASTM D1525 1 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 240 | °C | UL 746 |
| RTI Str | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 180 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® FC 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ULTEM™ CRS5011 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| GPP™ NH3 Natural | S&E Specialty Polymers, LLC | PP, Unspecified | GPP™ |
| Hostacom BG749GC/3 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ LC006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |