Next Nylon 6 Prime Series NST45-01BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lVgzq7_Next-Nylon-6-Prime-Series-NST45-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Un Filled Super Tough Heat Stabilized Black compound Product Applications Typical application such as cable and rope jacketing. Hose inners cores, fasteners & ski binding parts. Benefits High flexibility & good heat stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.05 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.95 | -- | % | |
| Across Flow | 1.4 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.4 | -- | % | |
| Saturation 1 | 7.8 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 850 | 400 | MPa | ASTM D638 |
| Tensile Strength | 45.0 | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 50 | > 200 | % | ASTM D638 |
| Flexural Modulus | 850 | 400 | MPa | ASTM D790 |
| Flexural Strength | 50.0 | 35.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 140 J/m | No Break | ||
| 23°C | 780 J/m | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 85.0 | -- | °C | |
| 1.8 MPa, Unannealed | 45.0 | -- | °C | |
| Melting Temperature | 218 | -- | °C | ASTM D2117 |
| CLTE | ASTM D696 | |||
| Flow : 23 to 55°C | 1.3E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.4E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 235 | °C | |
| Front Temperature | 235 to 240 | °C | |
| Mold Temperature | 45.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 7128B | UBE America, Inc. | Nylon 612 | UBE Nylon |
| WPP PP JOSB26287 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Huaxia Shenzhou FKM DS2603-2 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| Petrotene® PP A3 G30 NTLA010 PH316 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| CYCOLAC™ MG38F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |