Nylene® PX3422

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lVSNsw_Nylene-PX3422.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Heat stabilized, high impact modified nylon resin designed for maximum toughness with minimum sacrifice in tensile strength and melting point

Offers outstanding elongation and good retention of that elongation after 5 days of heat aging at 177°C (95% elongation)

Optimum processing conditions should provide a melt temperature of 490 - 530°F at the die

Suitable for processing in either extrusion or injection molding applications

General Information
Additive	Heat Stabilizer Impact Modifier
Features	Good Heat Aging Resistance Good Toughness Heat Stabilized Impact Modified
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.07	g/cm³	ASTM D792

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	44.1	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	310	%	ASTM D638
Flexural Modulus (23°C)	1450	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	1100	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	42.0	°C	ASTM D648
Peak Melting Temperature	214	°C	ASTM D3418

Injection	Nominal Value	Unit
Processing (Melt) Temp	254 to 277	°C

Extrusion	Nominal Value	Unit
Melt Temperature	254 to 277	°C

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC M1384	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Quadrant EPP ERTALON® 4.6	Quadrant Engineering Plastic Products	Nylon 46	Quadrant EPP
VITAMIDE® BI12	A. Schulman Europe	Nylon 6	VITAMIDE®
HM10® S5	Heritage Plastics, Inc.	LLDPE	HM10®
Karina RED COLOR CONCENTRATE 42/154-FC-LMP (SDB)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina