HAIPLEN H50 X2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lUALBg_HAIPLEN-H50-X2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer self extinguishing UL94 V2, good flow and surface finish. UL94 V2 approuved all colors at 1,5 mm Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized (D). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.3 | % | |
| Across Flow | 1.3 | % | |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 80 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180, ASTM D256 | ||
| -23°C | 25 | J/m | |
| 0°C | 30 | J/m | |
| 23°C | 35 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 120 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 1 | 65.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 4 2 |
| -- | 90.0 | °C | ASTM D1525, ISO 306/B 5 3 |
| Melting Temperature | 163 | °C | ASTM D211, ISO 121 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Needle Flame Test | VDE 0471/2 | ||
| 1.60 mm | Pass | ||
| 3.20 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 20000 hrs |
| 2 . | Loading 1 (10 N) |
| 3 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex NH-0825 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| WINDFORM® GF 2.0 | CRP Technology s.r.l. | Nylon, Unspecified | WINDFORM® |
| Baynat® 0759 BX Isocyanate | Covestro - PUR | PUR-MDI | Baynat® |
| Fainplast PVC PH 75/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| LNP™ COLORCOMP™ GX02708 compound | SABIC Innovative Plastics | PSU | LNP™ COLORCOMP™ |