LEXAN™ SFX173RU resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lTBQZU_LEXANSFX173RUresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SFX173RU is a transparent SecurFX grade with high flow, mold release and UV stabilizer. This grade is for security applications and contains proprietary authentication technology. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1570 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.0 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 8.0 | % | ASTM D638 |
| Fracture | 120 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2300 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 58.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 126 | °C | ASTM D648 |
| Vicat Softening Temperature | 144 | °C | ASTM D1525 6 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 260 - 282 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Nozzle Temperature | 266 - 288 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBN7052 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| WELLAMID Nylon 6600/50 GV 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Evermore PUR SS-1029MP | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| HIPLEX® HMN 6050 | HIP-PetroHemija | HDPE | HIPLEX® |
| Lupoy® GN5151RF | LG Chem Ltd. | PC+ABS | Lupoy® |