Order Products : sales@su-jiao.com
Vyncolit® 2923W
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lSgC2d_Vyncolit-2923W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® 2923W is a mineral filled phenolic molding compound with excellent heat resistance and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.75 | g/cm³ | ISO 1183 |
| Apparent Density | 0.78 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.42 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.070 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.2 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.72 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 11000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 100 | MPa | ISO 178 |
| Compressive Stress | 186 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 7.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 193 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.8E-5 | cm/cm/°C | TMA |
| Lateral | 5.1E-5 | cm/cm/°C | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.4E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.8E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Electrafil® M-2426 BK | Techmer Engineered Solutions | PC | Electrafil® |
| Hifax EKC 244X Black | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Hanwha Total PP TH24 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| POLYFLAM® RPP 1058UH | A. Schulman Inc. | PP, Unspecified | POLYFLAM® |
| Sylvin 8980-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |