TECACOMP® PPS TC grey 4083V
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lRrSeH_TECACOMPPPSTCgrey4083V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 | g/cm³ | |
| Apparent Density | 1.00 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (316°C/5.0 kg) | 150 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (316°C/5.0 kg) | 75.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.96 | % | ISO 294-4 |
| Flow | 0.93 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/50 |
| Tensile Stress | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 0.80 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 19 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 90.0 | °C | DIN 53765 |
| Melting Temperature | 280 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 100 to 200°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 100 to 200°C | 8.7E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.80 | W/m/K | DIN EN 821 |
| -- 2 | 0.90 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 230 | °C | |
| short term | 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 4.7E+13 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 300 - 370 | °C | |
| Mold Temperature | 140 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 TFE 10 Z | RTP Company | PBT | RTP |
| DENKA POVAL B-05 | Denka Company Limited | PVOH | DENKA POVAL |
| INTOL® 1500 | Versalis S.p.A. | SBR, Emulsion | INTOL® |
| LNP™ THERMOCOMP™ OF008A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ THERMOCOMP™ |
| Petrothene® NA860241 | LyondellBasell Industries | LDPE | Petrothene® |