Moplen EP340S
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lRKQVs_Moplen-EP340S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP340S is a high fluidity, nucleated heterophasic copolymer used for injection moulding applications. It offers outstanding processability, productivity and dimensional stability in combination with good impact behavior at low temperature. Moplen EP340S is extensively used in large items with impact requirements such as boxes, crates, pails, large household articles and some smaller items such as thin-walled containers, caps and flower pots. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 42 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 57.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 53.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 0°C | 4.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 120 | kJ/m² | |
| 0°C | 150 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -54.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/A50 |
| -- | 67.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 70 | ASTM D2457 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 7823 | LyondellBasell Industries | PP Copolymer | Pro-fax |
| Sylvin 9909-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ GF1311R resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| AXLENE® 12RM | INDELPRO, S.A. de C.V. | PP Random Copolymer | AXLENE® |
| Sylvin 9774-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |