PALSTYROL® R S M 12

Category:	PS (GPPS) , General Purpose Polystyrene
Manufacturer:	pal plast GmbH
Trademark:	PALSTYROL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lQZIQu_PALSTYROL-R-S-M-12.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALSTYROL®R S M 12 is a general-purpose polystyrene product,. It can be processed by extrusion or injection molding and is available in Europe. PALSTYROL®The application areas of R S M 12 include packaging, electrical/electronic applications and home applications. Features include: flame retardant/rated flame Copolymer Impact resistance

General Information
Features	Copolymer Medium impact resistance
Uses	Packaging Electrical/Electronic Applications Household goods
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.05	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (200°C/5.0 kg)	6.00	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2000	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	29.5	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	1.5	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	28	%	ISO 527-2/1A/50

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	82.5	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	550	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 200°C/5 kg: 4 to 8 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1900 to 2100 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 28 to 31 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 1 to 2 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 25 to 30 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 85 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³

Additional Information

Melt-Volume Flow Rate, ISO 1133, 200°C/5 kg: 4 to 8 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1900 to 2100 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 28 to 31 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 1 to 2 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 25 to 30 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 85 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³

Resin Grade	Manufacturer	Category	Trademark
TECOLITE KM-50BD	KYOCERA Chemical Corporation	Phenolic	TECOLITE
Ultramid® A3EG7 BK23189	BASF Corporation	Nylon 66	Ultramid®
Nycal™ 2050R30	Technical Polymers, LLC	Nylon 612	Nycal™
Beetle® PBTS120S	Teknor Apex Company (Chem Polymer)	PBT	Beetle®
PETILEN I22-19T	PETKIM Petrokimya Holding A.S.	LDPE	PETILEN