| Novalloy-S S69P1 is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific. Primary attribute of Novalloy-S S69P1: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2640 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 102 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 220 to 260 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemical Resources BPP3000 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| Estane® AG 9550 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| DIALAC® U400 | UMG ABS, Ltd. | MMBS | DIALAC® |
| ICORENE® 1877 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| SQUARE® LSR1966-34A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |