Nypol® PA A3 G20 NTLA010 NR401
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lNlOcG_Nypol-PA-A3-G20-NTLA010-NR401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 20% of fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.29 to 1.30 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | -- | % | ASTM D570 |
| Ash Content | 18 to 22 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 130 | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5300 | 3000 | MPa | ASTM D790 |
| Flexural Strength | 190 | 140 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 60 | 70 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Elvax® 3124 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Kotex KGN-30MRA | Kotec Corporation | PC | Kotex |
| Lucofin® 7410 HFFR | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| POLIMAXX GA850 | IRPC Public Company Limited | ABS | POLIMAXX |
| ULTEM™ ATX3562R resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |