Eltex® EXP9320
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lNZoKG_Eltex-EXP9320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Eltex® EXP9320 is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Eltex ® EXP9320 is formulated with antioxidants, slip and antiblock additives and a processing aid. Addition of other polymers, masterbatch and pigments may alter film slip and antiblock performance. Applications Eltex® EXP9320 has been developed for use in food packaging and other thin film applications where excellent mechanical and optical performance is required.. Eltex® EXP9320 offers easy extrudability We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® EXP9320 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.3 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | < 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% Secant, MD : 25 µm | 180 | MPa | |
| 1% Secant, TD : 25 µm | 200 | MPa | |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 25 µm | 9.00 | MPa | |
| TD : Yield, 25 µm | 10.0 | MPa | |
| MD : Break, 25 µm | 65.0 | MPa | |
| TD : Break, 25 µm | 60.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 25 µm | 550 | % | |
| TD : Break, 25 µm | 670 | % | |
| Dart Drop Impact (25 µm) | > 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 200 | g | |
| TD : 25 µm | 440 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 65 | ASTM D2457 | |
| Haze (25.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Conditioning ISO 1872/1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tisarbon® PC UNR FR | Tisan | PC | Tisarbon® |
| Capran® 1200T | Honeywell | Nylon 6 | Capran® |
| CERTENE™ LDF-820A | Muehlstein | LDPE | CERTENE™ |
| KOPELEN JM-350 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Sylvin 8200-60LG Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |