Kepamid® 1325M7
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lNWvWE_Kepamid-1325M7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kepamid 1325M7 is a 25% mineral filled, reinforced polyamide-6. Low warpage and good thermal properties. It is applicable to automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 77.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5980 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 205 | °C | |
| 1.8 MPa, Unannealed | 140 | °C | |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 230 to 250 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sultron® R20 | Asia International Enterprise (Hong Kong) Limited | PPS | Sultron® |
| Taitalac® 8520 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Vi-Chem PVC VNC87-30I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| CarmelStat™ CS 6015 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| LNP™ LUBRICOMP™ LGL33 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |