Plenco 05118 (Injection)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lNP0WG_Plenco-05118-Injection-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorption, and excellent dimensional stability under severe exposure. 05118 is available in gray. 05118 is not recommended for electrical insulating applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | ASTM D792 |
| Apparent Density | 0.89 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.35 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 58 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13300 | MPa | ASTM D638 |
| Tensile Strength | 39.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 11100 | MPa | ASTM D790 |
| Flexural Strength | 64.6 | MPa | ASTM D790 |
| Compressive Strength | 128 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 16.1 | J/m | ASTM D256 |
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 180 | °C | ASTM D648 |
| Continuous Use Temperature | 202 | °C | ASTM D794 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.07%Drop Ball Impact, PLENCO Method: 59 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 165 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-269H-1000 | Ravago Manufacturing Americas, LLC | PE, Unspecified | Ravago Compounds |
| Kumho KBR 710H | Korea Kumho Petrochemical Co., Ltd. | PBR, Low Cis | Kumho KBR |
| LCA® N66-101 Type | UniPlas, Inc. | Nylon 66 | LCA® |
| KEBAFORM® C 901 TF | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| MAJ'ECO BT360BS | AD majoris | Biodeg Polymers | MAJ'ECO |