| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lMLuu7_Cevian--V-680-680SF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V 680, 680SF is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific. Primary attribute of Cevian®-V 680, 680SF: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 55 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 42.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 130 | J/m | |
| 23°C, 6.40 mm | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 86.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 76.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Ball Pressure Test | 90 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF30-60 42LH-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Bormed™ RF825MO | Borealis AG | PP Random Copolymer | Bormed™ |
| Arnite® A02 307 | DSM Engineering Plastics | PET | Arnite® |
| Electrafil® ABS CF20 BK | Techmer Engineered Solutions | ABS | Electrafil® |
| Magnobond 104-228 | Magnolia Plastics, Inc. | Epoxy | Magnobond |