Durethan® AKV 35 H2.0 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lK2TyE_DurethanAKV35H20901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 35 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.41 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 300°C, 2.00mm 1 | 0.91 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.070 | -- | % | ISO 2577 |
| Flow direction : 300°C, 2.00mm 3 | 0.37 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.050 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 220 | 140 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 10300 | 6600 | MPa | ASTM D638 |
| 23°C | 11200 | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 200 | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.1 | 6.4 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 7000 | MPa | ISO 899-1 |
| 1000 hr | -- | 5800 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 9300 | 6400 | MPa | ASTM D790 |
| 23°C 5 | 10500 | 6500 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 5.0% strain, 23°C | 280 | 160 | MPa | ASTM D790 |
| 23°C | 300 | 200 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 280 | 165 | MPa | ISO 178/A |
| 23°C 6 | 300 | 200 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.1 | 6.2 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8(> 1.00 mm) | 29 | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-110, GF35 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 75 | kJ/m² | ISO 179/1eU |
| 23°C | 85 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 12 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | -- | kJ/m² | ISO 180/1U |
| 23°C | 75 | -- | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 2.60 | -- | J | ISO 6603-2 |
| 23°C | 3.20 | 5.90 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 830 | -- | N | ISO 6603-2 |
| 23°C | 900 | 1260 | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | ||||
| -- | 230 | -- | °C | ISO 306/B50 |
| -- | 250 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (254°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 9 | 263 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 35 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.00 | 10.0 | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.011 | 0.21 | IEC 60250 | |
| 23°C, 1 MHz | 0.015 | 0.065 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 425 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 600 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 10 | 25 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CROSSVINIL EK/10 EZ | Crosspolimeri S.p.A. | PVC, Unspecified | CROSSVINIL |
| Ferro PP TPP40AE57BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Tunhe PET TH102B | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |
| Hifax TRC 790X HF | LyondellBasell Industries | TPO (POE) | Hifax |
| Sylvin 8940-85FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |