ECO PELLET® LA13A
| Category: | PLA+ABS , Polylactic Acid + ABS |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | ECO PELLET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lIr0rf_ECO-PELLET-LA13A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ECO PELLET® LA13A is a Polylactic Acid + ABS (PLA+ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of ECO PELLET® LA13A are:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.50 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 48.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 27 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 70.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S-211 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Armlen® PP SM 20-4UP | Poly Plastic | PP, Unspecified | Armlen® |
| HANWHA CLNA-8141SC | Hanwha Chemical | LDPE | HANWHA |
| KetaSpire® KT-XXXX | Solvay Specialty Polymers | PEEK | KetaSpire® |
| Karina ORANGE COLOR CONCNETRATE 32/ 82-FC-(CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |