Durethan® BKV 35 H2.0 EF 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lIGQwF_DurethanBKV35H20EF901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 35 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.40 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.65 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.15 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.21 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.050 | -- | % | ISO 294-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 210 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10800 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 180 | 115 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10000 | 5900 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | -- | 150 | MPa | ISO 178/A |
| 23°C | 275 | 180 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.4 | 6.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-100, GF35 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 12 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 85 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | 10 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | 55 | kJ/m² | ISO 180/1U |
| 23°C | 70 | 75 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 160 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.7E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 216 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Starglas CF006 | Eurostar Engineering Plastics | TES | Starglas |
| UNISOFT ADHESION™ AD-35A-CL-8-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |
| BorPure™ RE450MO | Borealis AG | PP Random Copolymer | BorPure™ |
| Elastron® G P.G401.A45.701 | Elastron USA, Inc. | SEBS | Elastron® G |