Petrotene® PP A3 C60 NTLA010 PH317 MSM
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lGNXUO_Petrotene-PP-A3-C60-NTLA010-PH317-MSM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer reinforced with 60% calcium carbonate (CaCO3) for injection molding, combination of stiffness, impact and aesthetics of surface, good set of mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 to 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Ash Content | 58 to 62 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 120 | °C | |
| 1.8 MPa, Unannealed | 70.0 | °C | |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NatureFlex™ 90NVS | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| LUVOCOM® 1/SCF/30 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hostacom EKC 330N C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 9604-80 CLEAR 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ HFD1731 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |