Rotec® ABS 1002 FR V0/5
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lGAmLg_RotecABS1002FRV05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rotec®ABS 1002 FR V0/5 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in Europe, and the processing method is injection molding. Rotec®The main features of ABS 1002 FR V0/5 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 37 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 38.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 35 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 88.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 5VA | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 680K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Stylac™ 183 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| BMC 2270 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Karina IVORY PVC COMPOUND 951-35/4-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADVANCENE™ EE-5001-PAB | ETHYDCO | HDPE | ADVANCENE™ |