Derakane® Momentum 470-300
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | Ashland Performance Materials |
| Trademark: | Derakane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lFweW3_Derakane-Momentum-470-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DERAKANE MOMENTUM 470-300 resin is a novolac-based vinyl ester designed to provide exceptional mechanical properties at higher temperatures. This resin offers a high resistance to solvents and chemicals, good retention of strength and toughness at elevated temperatures, and excellent resistance to acidic oxidizing environments. DERAKANE MOMENTUM resins are a new generation of resins that can be used to improve fabrication efficiency and product quality. Their lighter color makes defects easier to see and correct while the resin is still workable. The longer stability provies additional flexibility to fabricators in storage and handling. APPLICATIONS AND USE DERAKANE MOMENTUM 470-300 resin is suitable for applications involving high temperature chlorination or caustic scrubbing and storage, industrial waste treatment facilities and solvent extraction processes used in mining. It is also used for hydrochloric acid transport, tank, truck and railcar linings, and gasohol storage. DERAKANE MOMENTUM 470-300 is recommended for most commercial FRP fabrication processes including hand lay-up, spray-up, pultrusion and resin transfer molding. The higher viscosity of MOMENTUM DERAKANE 470-300 resin facilitates filament winding and contact molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Solution Viscosity | 325 | mPa·s | |
| Styrene Content | 33 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Volume Shrinkage | 8.3 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 40 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 3590 | MPa | ASTM D638 |
| -- | 3600 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 86.2 | MPa | ASTM D638 |
| -- | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield) | 3.0 - 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 3790 | MPa | ASTM D790 |
| -- | 3800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 131 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Glass Transition Temperature | |||
| -- | 166 | °C | ASTM D3418 |
| -- | 165 | °C | ISO 11357-2 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Properties of cured casting at 25°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vatpol 305 | Vatan Plastik San. Tic. AS | PE, Unspecified | Vatpol |
| UNISOFT TPE™ ST-85A-CL-7-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| CYCOM® 7714A | Cytec Industries Inc. | Epoxy | CYCOM® |
| LNP™ THERMOTUF™ RN001IX4 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOTUF™ |
| TABOREN® PH 41 G 30-095 | SILON s.r.o. | PP Homopolymer | TABOREN® |