Zytel® RS 32CG20HSL BK409
| Category: | Nylon 610 , RENEWABLY SOURCED™ POLYAMIDES* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lDH2Io_Zytel-RS-32CG20HSL-BK409.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Carbon/Glass Reinforced, Renewably Sourced, Polyamide 610 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 9900 | -- | MPa | ISO 178 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glass Transition Temperature 1 | 60.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 224 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ EPDM0366-NC | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| PRL PPX-SF1 | Polymer Resources Ltd. | PPE+PS | PRL |
| ULTEM™ EXUM0169 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ENPRENE 655 | En Chuan Chemical Industries Co,. Ltd. | SBS | ENPRENE |
| Sylvin 8260-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |