LG ASA LI923
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lDAUCP_LG-ASA-LI923.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: Good Weatherability, High Rigidity Application: Communication Instrument Cover, Cable Connecting Cover, Door Panel |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2150 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20mm | > 6.0 | % | ASTM D638 |
| Fracture, 3.20mm | 25 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 77.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 39 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 39 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 97.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 89.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 210 - 230 | °C | |
| Cylinder Zone 4 Temp. | 210 - 230 | °C | |
| Adapter Temperature | 210 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 210 - 250 | °C |
| Extrusion instructions |
|---|
| Minimum Moisture Content: 0.01%Roll Stack Temperature: Top: 70 to 90 °C Middle: 70 to 90 °C Bottom: 70 to 100 °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP482V | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| Karina WHITE PVC COMPOUND BT-0002/17 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8200-75 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EnviroPBT 1001 | West Michigan Compounding | PBT | EnviroPBT |
| Hifax TRC 790PHF 3004 BLK | LyondellBasell Industries | TPO (POE) | Hifax |