Starex LD-0955
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lBlEP1_StarexLD0955.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex LD-0955 is a polymethyl methacrylate-acrylic acid product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical appliances. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.30 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.30 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.30 | % | ISO 2577 |
| Traffic : 3.20mm | 0.30 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 117 | ASTM D785 | |
| R scale | 117 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2500 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 34.0 | MPa | ASTM D638 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 25 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2400 | MPa | ASTM D790 |
| -- 6 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 79.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 20 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 20 | J/m | ASTM D256 |
| 23°C 11 | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C, 3.18 mm | 260 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 250 | J/m | ASTM D256 |
| -5°C 12 | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 99.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 79.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| 12 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V76F | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| RTP 204H FR | RTP Company | Nylon 66 | RTP |
| CALP E4362K | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Fainplast PVC PK 7075 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Rotuba CAB B902 (20% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |