SABIC® LDPE 2101N0W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lBf0ou_SABIC-LDPE-2101N0W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2101N0W is a grade with good toughness and biaxial shrink properties. The material contains no additives, has a low energy consumption during processing and a good draw down ability. Application SABIC® LDPE 2101N0W is typically used for thin shrink film. SABIC® LDPE 2101N0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 170 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 170 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 250 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 50 | g | Internal method |
| Re-blocking - Blown Film (50.0 µm) | 50 | g | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 40.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 30.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 9.0 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at 50 µm film with a BUR of 3.The film has been produced on Kiefel IBC film blown line at 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMAPET® P184 | Indorama Ventures PCL | PET | RAMAPET® |
| AKROMID® A3 GF 25 3 black (3094) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| DENKA Transparent Polymer TH-21 | Denka Company Limited | MMBS | DENKA Transparent Polymer |
| Geon™ Vinyl Wire & Cable WEMB410A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Amodel® AE-8935 | Solvay Specialty Polymers | PPA | Amodel® |