TUFLIN™ HS-7098D NT 7

Category:	LLDPE , Linear Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	TUFLIN™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lBCNod_TUFLINHS7098DNT7.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

TUFLIN™ HS-7098D NT 7 is an ethylene-hexene copolymer, linear low density polyethylene (LLDPE) resin designed for cast and blown film applications such as trash bags, industrial can liners, and retail bags. Films extruded with HS-7098D NT 7 exhibit superb toughness, high tensile strength and elongation, excellent tear and puncture resistance, and are readily heat sealable.

Main Characteristics:

Hexene Linear Low Density Resin

High strength

Excellent toughness

Complies with:

U.S. FDA 21 CFR 177.1520(c)3.1a (with Restrictions). An additive present in this product limits use only in film form for food contact applications.

Application:

Heavy Duty Industrial and Consumer Liners

General Information
Additive	Processing aid Anti-caking agent (2500 ppm) Sliding agent (1000 ppm)
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Blow film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.923	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Strength			ASTM D882
MD : Break, 25 µm	44.8	MPa	ASTM D882
TD : Break, 25 µm	34.5	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 25 µm	500	%	ASTM D882
TD : Break, 25 µm	700	%	ASTM D882
Dart Drop Impact ¹(25 µm)	200	g	ASTM D1709A
Elmendorf Tear Strength ²			ASTM D1922
MD : 25 µm	310	g	ASTM D1922
TD : 25 µm	800	g	ASTM D1922

Optical	Nominal Value	Unit	Test Method
Gardner Gloss (45°, 25.4 µm)	45		ASTM D523
Haze (25.4 µm)	16	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	231	°C

Extrusion instructions
吹塑薄膜的制造条件：螺杆尺寸：2.5 英寸 (63.5 mm) 30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 熔体温度：448 °F (231 °C) 输出：模具周长的 6 磅/小时/英寸模具直径：6 英寸放大比：2.5 比 1 螺杆速度：78 rpm 冷冻线高度：25 英寸 (635 mm) 1% 割线模量

Note Message
1 .	F50
2 .	Method B

Resin Grade	Manufacturer	Category	Trademark
POLYMAN® (ABS) LC 165	A. Schulman Europe	ABS	POLYMAN®
Sindustris PP HI5303RB	Sincerity Australia Pty Ltd.	PP, Unspecified	Sindustris PP
Adell Polyamide AJ-17	Adell Plastics, Inc.	Nylon 66	Adell Polyamide
Hifax HSBMCB1158ACLS/2	LyondellBasell Industries	TPO (POE)	Hifax
OnFlex™ S KG 60A-3S2018	PolyOne Corporation	TPE	OnFlex™