RTP 6004-55A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lAAxQA_RTP-6004-55A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyolefin Elastomer (TEO) - Nylon 6 Overmolding |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 - 2.0 | % | ASTM D955 |
| Moisture Content | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel strength- Nylon 6 1 | 4.4 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 58 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break, 3.20 mm) | 3.45 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 350 | % | ASTM D412 |
| Tear Strength 4 | 16.6 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 216 - 249 | °C | |
| Mold Temperature | 48.9 - 65.6 | °C |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | 90°, 20 in/min, RTP 55, Interface Failure |
| 2 . | C mold, 500 mm/min |
| 3 . | Mouth die C, 500 mm/min |
| 4 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 361 | RTP Company | PC | RTP |
| Ultradur® B 4300 M5 | BASF Corporation | PBT | Ultradur® |
| Nycal™ 2050R33H | Technical Polymers, LLC | Nylon 612 | Nycal™ |
| Iupital® F20-54 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| PETILEN I15-19T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |