NORYL GTX鈩?GTX679 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l8m0wn_NORYL-GTX-GTX679-resin-50561.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to allow for primer-less electrostatic painting. GTX679 has improved impact/elongation and the mineral content enables the material to be used in structural applications replacing metal or thermoset resins. The material is only available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4450 | MPa | ASTM D638 |
| -- | 4790 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 62.0 | MPa | ASTM D638 |
| Fracture | 61.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 5 | 4.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 4000 | MPa | ASTM D790 |
| -- 7 | 4440 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 109 | MPa | ISO 178 |
| Fracture, 50.0mm span 8 | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 3.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 31 | J/m | ASTM D256 |
| 23°C | 39 | J/m | ASTM D256 |
| -30°C 10 | 3.5 | kJ/m² | ISO 180/1A |
| 23°C 11 | 4.2 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 7.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 185 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 184 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 188 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 260 - 299 | °C | |
| Middle Temperature | 266 - 299 | °C | |
| Front Temperature | 271 - 299 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9875H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| NEOPLAST 180 M/E | Zylog Plastalloys | TPE | NEOPLAST |
| Braskem PE BF4810 | Braskem | HDPE | Braskem PE |
| Axiall PVC 18650 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina BLACK PVC COMPOUND 858-48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |