LUVOCOM® 50-8779 Datasheet,PC,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®50-8779 is a polycarbonate (PC) material,. This product is available in Europe,. LUVOCOM®The main features of 50-8779 are: Conductivity Good dimensional stability Typical application areas include: Electrical/electronic applications engineering/industrial accessories business/office supplies Sporting goods medical/health care

General Information
Features	Good dimensional stability Heat conduction
Uses	Electrical/Electronic Applications Engineering accessories Business equipment Sporting goods Medical/nursing supplies
Appearance	Grey

Physical	Nominal Value	Unit	Test Method
Density	1.39	g/cm³	ISO 1183
Molding Shrinkage	0.40 - 0.70	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.20	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10000	MPa	ISO 527-2
Tensile Stress (Break)	41.0	MPa	ISO 527-2
Tensile Strain (Yield)	0.70	%	ISO 527-2
Flexural Modulus	8500	MPa	ISO 178
Flexural Stress	62.0	MPa	ISO 178
Flexural Strain at Flexural Strength	1.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	150	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	7.0	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	130	°C	UL 746B
Thermal Conductivity ¹	17	W/m/K

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+3	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0 - 6.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	280 - 300	°C
Middle Temperature	290 - 310	°C
Front Temperature	300 - 320	°C
Nozzle Temperature	290 - 310	°C
Processing (Melt) Temp	295	°C
Mold Temperature	80.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Hot-Disk, 60x60x3 mm

Category:	PC , Polycarbonate
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	l7VIEE_LUVOCOM-50-8779.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SUMIPEX® LG35	Sumitomo Chemical Co., Ltd.	Acrylic (PMMA)	SUMIPEX®
Moplen RP344NK	PolyMirae	PP Random Copolymer	Moplen
Clariant PC PC-1100G20	Clariant Corporation	PC	Clariant PC
Fluon® PTFE RB1020S	Asahi Glass Co., Ltd.	PTFE	Fluon®
Infino XP-2165MC	SAMSUNG SDI CO., LTD.	PPS	Infino