Lotader® 4210

Category:	EBA , Ethylene Butyl Acrylate Copolymer
Manufacturer:	Arkema
Trademark:	Lotader®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	l3Wv6e_Lotader-4210.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LOTADER® 4210 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

Applications
LOTADER® 4210 is a versatile adhesive for extrusion coating or lamination, designed as:

Concentrate to be used in dry blend with LDPE. LOTADER® 4210 improves adhesion of LDPE on aluminium foils, metallized or primerized films.

Ready for use resin to be used pure. LOTADER® 4210 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and its copolymers.

Coextrusion tie layer for PE/PA in extrusion coating process.

General Information
Features	Good Adhesion High Melt Stability Terpolymer
Uses	Adhesives Coating Applications Laminates Tie-Layer
Forms	Pellets
Processing Method	Extrusion Extrusion Coating Laminating

Physical	Nominal Value	Unit	Test Method
Density	0.940	g/cm³	ISO 1183, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	9.0	g/10 min	ASTM D1238, ISO 1133
n-Butyl Acrylate Content	6.5	wt%
Maleic Anhydride Content	3.6	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness
Shore D, Compression Molded	46		ASTM D2240
Shore D, Compression Molded	69		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	10.0	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	650	%	ASTM D638, ISO 527-2
Flexural Modulus (Compression Molded)	120	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	69.0	°C	ISO 306/A, ASTM D1525 ¹
Melting Temperature	105	°C	ISO 11357-3

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene HP519-00	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
Abstron IM17AHF	Bhansali Engineering Polymers Limited	ABS	Abstron
Alpha PVC 3006-90 CLEAR 0217	AlphaGary	PVC, Flexible	Alpha PVC
Celanex® 3300D	Celanese Corporation	PBT	Celanex®
LUVOCOM® 65-8961/ES	LEHVOSS Group	PP Copolymer	LUVOCOM®