Baytec® MS-092 (HQEE)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l33x7S_Baytec-MS-092-HQEE-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec MS-092 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer. It is used in the manufacture of high-property solid cast polyurethane elastomers. As with any product, use of Baytec MS-092 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 42.0 | mg | ASTM D3498 |
| Compression Deflection | ASTM D575 | ||
| 10% | 4.83 | MPa | ASTM D575 |
| 15% | 8.96 | MPa | ASTM D575 |
| 2% | 0.827 | MPa | ASTM D575 |
| 20% | 22.8 | MPa | ASTM D575 |
| 25% | 33.1 | MPa | ASTM D575 |
| 5% | 3.45 | MPa | ASTM D575 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 13.1 | MPa | ASTM D412 |
| 200% strain | 15.5 | MPa | ASTM D412 |
| 300% strain | 19.3 | MPa | ASTM D412 |
| Tensile Strength (Break) | 42.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 118 | kN/m | ASTM D624 |
| Cracking | 66 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 26 | % | ASTM D395 |
| Bayshore Resilience | 42 | % | ASTM D2632 |
| Additional Information |
|---|
| Appearance: Pale yellow liquidNCO: 8.95 to 9.34 wt%Flash Point, PMCC: 222°CSpecific Gravity at 80°C: 1.15Specific Gravity at 100°C: 1.13Viscosity at 80°C: 750 mPa-sViscosity at 100°C: 365 mPa-sNCO/OH Ratio: 1.10Stoichiometry: 90% TheoryPrepolymer Temperature: 90 to 100°CExtender Temperature: 100 to 110°CMold Temperature: 100 to 110°CPot Life: 2 to 4 minDemold: 30 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® C015EG | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| TECHNYL STAR™ SX 218 V50 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Celcon® WR90Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Durez® 33830 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| NORYL GTX™ GTX840 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |