Anjacom® 036/80
| Category: | Nylon 6+ASA , Polyamide 6 + ASA |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l2ugH5_Anjacom-036-80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anjacom® 036/80 is a Polyamide 6 + ASA (Nylon 6+ASA) material. It is available in Europe. Primary attribute of Anjacom® 036/80: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 2.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 2.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® 18 SR FD | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| XANTAR® 27 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| ADENE GNOBG | A.D. Compound spa | PP Copolymer | ADENE |
| Keyflex® BT 2140D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Hifax TYC 337P 3 S81466 | LyondellBasell Industries | PP Copolymer | Hifax |