LNP™ LUBRICOMP™ PFL36 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l2fbOQ_LNPLUBRICOMPPFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP PFL36 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound PFL-4036 Product reorder name: PFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 7880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 110 | MPa | ASTM D638 |
| Yield | 113 | MPa | ISO 527-2 |
| Fracture | 110 | MPa | ASTM D638 |
| Fracture | 113 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.8 | % | ASTM D638 |
| Yield | 4.1 | % | ISO 527-2 |
| Fracture | 6.7 | % | ASTM D638 |
| Fracture | 4.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Stress | 172 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 79 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 19.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 216 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 216 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 201 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 202 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 266 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC87-30I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Yanshan PE LD166 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Hostacom TYC 240N Black | LyondellBasell Industries | PP Copolymer | Hostacom |
| POLIMAXX 2563PCXTA6 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| Sumiliteresin® PR-CEL-6C | SBHPP | Phenolic | Sumiliteresin® |