Alkathene® WJG117
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l1OkqM_Alkathene-WJG117.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WJG117 is a low flow low density polyethylene which offers a high level of toughness. WJG117 is suited to thick section mouldings, caps and closures requiring a high level of toughness. WJG117 is not recommended for high stress crack resistant applications. Suitability for use in any application should be determined by appropriate performance testing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 49 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 1.90 mm | 10.4 | MPa | |
| Break, 1.90 mm | 13.2 | MPa | |
| Tensile Elongation 2(Break, 1.90 mm) | 620 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 200 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 108 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Type IV, 500 mm/min |
| 3 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 LF Z | RTP Company | PEEK | RTP |
| RTP ESD C 2800 B-45A Black | RTP Company | TPO (POE) | RTP |
| Mediprene® A2 500450M | ELASTO | SEBS | Mediprene® |
| TOTAL Polypropylene PPR 6232 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| OxyVinyls® 185 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |