Boda BDTL30P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l0Adi5_Boda-BDTL30P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDTL30P is a high viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good flowability and superior low temperature flexibility than standard terpolymers are required. BDTL30P can be compounded to meet the major fluoroelastomer specifications. BDTL30P can be used for injection, calendering, extrusion and compression molding of articles. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 30 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 1.85 | N·m | |
| ML 2(177°C) | 0.200 | N·m | |
| t'90 3(177°C) | 2.3 | min | |
| ts2 4(177°C) | 2.3 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Tr10 | -18 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 76 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 220 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 26 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Brittleness Temperature | -40.0 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 33 GF BLK/BLK | RTP Company | Nylon 66 | RTP |
| SCHULABLEND® (PC/ABS) M/MB 5 GF 10 | A. Schulman Europe | PC+ABS | SCHULABLEND® |
| TRISTAR® PC-10R-(8) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| LNP™ STAT-KON™ DX09301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| OTECH ALLOY OW128WLG - A/V Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |