SABIC® PPcompound 7705
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kzueyf_SABICPPcompound7705.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 7705 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, scratch resistance, and heat stability with interior automotive UV stability. The IMDS is 16161010. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1910 | MPa | ASTM D638 |
| -- | 2010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 23.0 | MPa | ASTM D638 |
| Yield | 22.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 16.0 | MPa | ASTM D638 |
| Fracture | 17.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 4.6 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2/50 |
| Fracture 5 | 24 | % | ASTM D638 |
| Fracture | 32 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 64.0mm span 6 | 2080 | MPa | ISO 178 |
| 50.0mm span 7 | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 2.4 | kJ/m² | ISO 179/1eA |
| 23°C 9 | No Break | ISO 179/1eA | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 10 | 120 | J/m | ASTM D256 |
| -30°C 11 | 3.0 | kJ/m² | ISO 180/1A |
| 0°C 12 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 14(23°C, 3.20 mm) | No Break | ASTM D4812 | |
| Instrumented Dart Impact 15 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 7.10 | J | ASTM D3763 |
| 0°C, Energy at Peak Load | 19.1 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 22.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 112 | °C | ASTM D648 |
| 0.45 MPa, not annealed 16 | 105 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.20mm | 57.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 17 | 59.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 59.0 | µm/Mk | ISO 11359-2 |
| Transverse : -30 to 100°C | 148 | µm/Mk | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 210 - 270 | °C | |
| Nozzle Temperature | 210 - 270 | °C | |
| Processing (Melt) Temp | 210 - 270 | °C | |
| Mold Temperature | 15.0 - 60.0 | °C | |
| Back Pressure | 1.00 - 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 63.5*12.7*3.2mm, Cut |
| 11 . | 80*10*4mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 80*10*4mm, Cut |
| 14 . | 63.5*12.7*3.2mm, Cut |
| 15 . | 6.60 m/sec |
| 16 . | 80*10*4mm, Cut |
| 17 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X5075 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC V861 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Axiall PVC 6300 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Geon™ Vinyl Flexible FC800 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ LUBRICOMP™ REL22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |