This data represents typical values that have been calculated from all products classified as: Generic HDPE - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 - 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.15 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 - 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 59 - 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1860 - 8280 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 29.6 - 75.8 | MPa | ASTM D638 |
| Fracture, 23°C | 40.8 - 55.7 | MPa | ASTM D638 |
| 23°C | 22.8 - 59.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.8 - 10 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 9.2 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1240 - 4230 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 29.0 - 91.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 52 - 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 260 - 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 121 - 130 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 - 122 | °C | ASTM D648 |
| CLTE - Flow | 4.8E-5 - 7.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 9.8E+15 - 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.5 - 79.5 | °C | |
| Drying Time | 2.0 - 2.5 | hr | |
| Rear Temperature | 231 - 246 | °C | |
| Middle Temperature | 231 - 246 | °C | |
| Front Temperature | 225 - 246 | °C | |
| Processing (Melt) Temp | 212 - 234 | °C | |
| Mold Temperature | 37.8 - 44.0 | °C | |
| Injection Pressure | 86.2 - 103 | MPa | |
| Back Pressure | 0.345 - 0.517 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic HDPE - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-506 | Lubrizol Advanced Materials, Inc. | PS (HIPS) | Stat-Rite® |
| ALTECH® PP-H A 4920/107 MR20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Andur 9200 AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Fluoroplex GF 313 - GML | UNIFLON | PTFE | Fluoroplex |
| K-vinyl 60 Deg C Rating Insulation (80-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |