Infino LB-1010W
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kzgQGK_Infino-LB-1010W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino LB-1010W is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 48 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 120 | ASTM D785 | |
| R-Scale | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 3 | 58.0 | MPa | ASTM D638 |
| Break | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 80 | % | ASTM D638 |
| Break | 87 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 77.0 | MPa | ASTM D790 |
| -- 8 | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 47 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 490 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 370 | J/m | ASTM D256 |
| 23°C 10 | 43 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 132 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 133 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 117 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 123 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ISO 306/B50 |
| -- | 141 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 110 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3487-1 | RTP Company | LCP | RTP |
| RX® 852 | Sumitomo Bakelite North America, Inc. | Phenolic | RX® |
| SEQUEL® 2430 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Hanwha Total PP BJ300 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| PENTESTER ET GV25 E H RC schwarz | PENTAC Polymer GmbH | PET | PENTESTER ET |