Zytel® HTN 54G35HSLR NC010
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kyfH0o_Zytel-HTN-54G35HSLR-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, Toughened, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | -- | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 11000 | MPa | |
| 1000 hr | -- | 10000 | MPa | |
| Flexural Modulus | 9000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 9.0 | -- | kJ/m² | |
| 23°C | 12 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 75 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 285 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 7.2E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 7.5E-5 | -- | cm/cm/°C | |
| Thermal Conductivity | 0.35 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Electric Strength | 43 | 42 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-124-28 | Quantum Composites Inc. | TS, Unspecified | Quantum Composites |
| RheTech Polypropylene P254-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SUMIKASUPER® LCP E6808LHF | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| HiFill® HDPE GF40 | Techmer Engineered Solutions | HDPE | HiFill® |
| Sylvin 83002-73 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |