Message
LUVOCOM®19-8942 is a polyamide 46 (nylon 46) material,. This product is available in Europe,. LUVOCOM®The main features of 19-8942 are: Wear-resistant Lubrication Typical application areas include: engineering/industrial accessories Electrical/electronic applications textile/fiber Automotive Industry business/office supplies

General Information
Additive	PTFE lubricant
Features	Low friction coefficient Good wear resistance Lubrication
Uses	Gear Textile applications Engineering accessories Switch Application in Automobile Field Business equipment Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.24	g/cm³	ISO 1183
Molding Shrinkage	1.3 - 2.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3500	MPa	ISO 527-2
Tensile Stress (Break)	75.0	MPa	ISO 527-2
Tensile Strain (Yield)	7.0	%	ISO 527-2
Flexural Modulus	2500	MPa	ISO 178
Flexural Stress	97.0	MPa	ISO 178
Flexural Strain at Flexural Strength	7.8	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	160	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	130	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	150	°C	UL 746B

Injection	Nominal Value	Unit
Drying Temperature
A	80.0	°C
Vacuum dryer, B	80.0	°C
Drying Time
A	2.0 - 8.0	hr
Vacuum dryer, B	2.0 - 12	hr
Suggested Max Moisture	0.10	%
Rear Temperature	285 - 315	°C
Middle Temperature	305 - 315	°C
Front Temperature	305 - 315	°C
Nozzle Temperature	280 - 330	°C
Processing (Melt) Temp	310	°C
Mold Temperature	120 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 46 , Polyamide 46
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kyWuYS_LUVOCOM-19-8942.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3868H	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
NITRIFLEX N-608	NITRIFLEX	NBR	NITRIFLEX
Beamset 101	Arakawa Chemical Industries, Ltd.	Epoxy	Beamset
ARCEL® 730 (3.00 pcf)	NOVA Chemicals	PS+PE	ARCEL®
Elastron® D P.D100.A40.N	Elastron USA, Inc.	SBS	Elastron® D