Generic ABS - Carbon Fiber
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kyUEPa_Generic-ABS---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.30 | g/cm³ | ASTM D792 |
| 23°C | 1.08 - 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.095 - 0.31 | % | ASTM D955 |
| 23°C | 0.20 - 0.30 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.14 - 0.21 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 108 - 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4460 - 23800 | MPa | ASTM D638 |
| 23°C | 5760 - 10400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 21.4 - 131 | MPa | ASTM D638 |
| Fracture, 23°C | 76.1 - 125 | MPa | ASTM D638 |
| Fracture, 23°C | 59.6 - 90.5 | MPa | ISO 527-2 |
| 23°C | 74.3 - 126 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.3 - 1.5 | % | ASTM D638 |
| Fracture, 23°C | 0.90 - 2.9 | % | ASTM D638 |
| Fracture, 23°C | 0.95 - 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1050 - 19700 | MPa | ASTM D790 |
| 23°C | 5290 - 6950 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 41.4 - 193 | MPa | ASTM D790 |
| 23°C | 45.0 - 216 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 46 - 55 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 150 - 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 102 - 118 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.4 - 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.6 - 102 | °C | ISO 75-2/A |
| CLTE - Flow | 1.8E-5 - 7.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.5 - 1.3E+10 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 5.0 - 1.3E+9 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.1 - 82.5 | °C | |
| Drying Time | 2.0 - 9.0 | hr | |
| Suggested Max Moisture | 0.075 - 0.10 | % | |
| Rear Temperature | 209 - 247 | °C | |
| Middle Temperature | 214 - 246 | °C | |
| Front Temperature | 215 - 271 | °C | |
| Nozzle Temperature | 210 - 235 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 59.8 - 80.6 | °C | |
| Injection Pressure | 85.9 - 103 | MPa | |
| Back Pressure | 0.258 - 0.556 | MPa | |
| Screw Speed | 45 - 71 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® P121 GR30 | Razin™ Engineering Plastics | PP Impact Copolymer | Razalen® |
| Sylvin 8672-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nypol® PA B3 HL NTLA010 NT308 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Karina WHITE PVC COMPOUND -E 801-10/ 43-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TOTAL Polyethylene Bio TPSeal® 1100_03 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |